Structural defects formation laws in the process of G18C2 alloy phase hardening

В. Й. Бондар, В. Ю. Данільченко, В. Є. Яковлев

Abstract


The work represents the experimental results of disorientation accumulation and chaotic stacking faults accumulation in the austenite and martensite phases in the process of cyclic γ-ε-γ-martensitic transformations in G18C2 alloy. Using X-ray method on mono- and polycrystalline samples it was shown that the accumulation of lattice disorientation of γ-and ε-phase of G18C2 alloy as a result of cyclic γ-ε-γ-transformations performed less intense than in iron-nickel alloys with γ-α-γ-type transformations. This difference can be explained by the higher reversibility of the direct γ-ε- and return ε-γ-transformations. Ψ lattice angle of reverted austenite even in the cace of intensive γ-ε-γ-cycling does not exceed (9-10) °. Thus, as a result of cyclic γ-ε-γ-transformations in Fe-Mn alloys can be formed only a low-angle fragments subboundaries of the original grain, and new reverted austenite grains with orientations that differ from the original grain orientation can’t be formed.


Keywords


martensitic transformation; the phase hardening; dislocation; stacking fault; nanofragments; diffraction

References


1. Малышев К. А., Сагарадзе В. В. Фазовый наклеп аустенитных сплавов на железоникелевой основе. – М.: Наука, 1982. – 260 с.
2. Данільченко В. Ю. Фізичні принципи формування нанокристалічного аустеніту залізонікелевих сплавів за допомогою циклічних мартенситних перетворень // МиНТ. – 2008. – Т.30, №10. – С. 1395-1411.
3. Сагарадзе В. В., Данильченко В. Е., Леритье Ф. Фазовый наклеп и образование нанокристаллического Fe-Ni-аустенита при мартенситных γ-α-γ- превращениях // ФММ. – 2001. – Т.92, №4. – С. 56-70.
4. Лысак Л. И., Николин Б. И. Физические основы термической обработки стали. – К.: Техника, 1975. – 304 с.
5. Бондарь В. И., Гиржон В. В., Данильченко В. Е. Влияние термоциклирования на мартенситное превращение в железоникелевых сплавах // ФММ. – 1991. – № 1. – С. 159-164.
6. Sagaradze V. V., Danilchenko V. E., L'Heritier Ph., Shabashov V. A. The structure and properties of Fe-Ni alloys with a nanocrystalline austenite formed under different conditions of gamma-alpha-gamma transformations // Materials Science and Engineering. – 2002. – A337. – P. 146-159.
7. Печковский Э. П., Трефилов В. И. Влияние структуры аустенита на развитие мартенситного превращения в сплавах на основе железа // УФЖ. – 1971. – 16. – C. 133-142.
8. Warren B. E., Warekols E. P. Stacking faults in cold worked alpha-brass // Acta Metall. – 1955. – 3. – P. 473.
9. Вишняков Я. Д. Дефекты упаковки в кристаллической структуре. – М: Металлургия, 1970. – 216 с.
10. Уоррен Б. И. Рентгенографическое изучение деформированных металлов // Успехи физики металлов. – 1963. – Вып. 5. – C. 172-237.
11. Paterson M. S. X‐Ray Diffraction by Face‐Centered Cubic Crystals with Deformation Faults // J. Appl. Phys. – 1952. – V. 23. – P. 805-809.
12. Богачев И. Н., Еголаев В. Ф. Структура и свойства железомарганцевых сплавов. – М: Металлургия, 1973. – 295 с.

13. Christian J. W. A note on deformation stacking faults in hexagonal close packed lattices // Acta Cryst. – 1954. – V. 7. – P. 415-416.


Full Text: PDF (Українська)
Archive
2013 16
2014 16
2015 16
2016 1
2017 1
2018 1
2019

1

User

Language

Journal Content

Browse